Filter Bag To Ensure That The Filter Effect To Meet The Emission Concentration

Filter bag as the heart of the bag filter, the effectiveness of the use of bag filter play a decisive role. In particular, the high temperature filter bag in the whole proportion of the value of a large number of dust collector to protect the filter bag to prevent damage due to various reasons, on the one hand, you can ensure that the filter effect to meet the emission concentration; the other hand, can reduce the economy Loss, to ensure the stable operation of the entire equipment.

filter bag damage type

Mechanical damage

Mainly for the filter non-woven layer of grinding, off, this phenomenon is due to uneven distribution of air flow, dust in the high filter wind speed on the filter bag surface erosion caused; or because the filter bag is not in place, resulting in bag The friction between the broken; or injection pipe installation is not vertical, resulting in the mouth of 30-40 cm range of holes, loss of filtration performance.

Specific performance in the filter bag mouth damage, bag bag bag damage, the lower part of the bag damage, the bottom of the bag damage.

dust filter bag pocket parts

Filter bag pocket parts damage more in the pocket down 30-40 cm within the performance of the bottom of the filter material blown, off off. Mostly for the compressed air is too high, the injection pipe skew, deformation of the board and other reasons, in the installation process to pay attention to the quality of installation.

bag bag body position

Filter bag and skeleton contact part of the long-term due to pulse jet caused by contact part of the wear and tear, the performance of the vertical and horizontal tendons in the direction of wear traces. Pay attention to the size of the filter bag and skeleton with the surface of the dust skeleton finish.

Bottom of the bag is damaged

Filter bag bottom phenomenon is more common wear and tear, may be due to the bottom of the bag cage is too small or bag too long, pocket can only be made under the bottom of the bag. Filter bag cleaning and filtration when the action is too large inside the bottom of the filter bag wear. Or dust accumulation is too high to form eddy current wear filter bag.

Chemical corrosion

The most obvious manifestation of chemical corrosion is the sharp drop in the strength of the dust bag, which is manifested in acid corrosion, alkali corrosion, oxidative corrosion and hydrolytic corrosion, which results in loss of acceptable filtration load and loss of filtration performance. This phenomenon is mainly due to the selection of filter bags or use the conditions of the environment beyond the scope of the fiber, resulting in filter bag loss of performance and failure.

Acid corrosion

High temperature filter is generally acid corrosion, mainly sulfur oxide. Especially in the coal-fired boiler power plant flue gas dust, the use of high-sulfur coal, and electronic bag with the project, the sulfur content of flue gas is high, can reach 5000mg / Nm3. In high temperature environment, sulfur oxides to form sulfurous acid, sulfuric acid, the filter caused by acid corrosion and failure. If the flue gas contains HF, you can not use glass fiber filter, easy acid corrosion caused by filter failure.

General control of flue gas operating temperature above the acid dew point can be, such as below the acid dew point temperature must be closed dust collector system, to avoid corrosion filter bag. Acidic liquids are hydrochloric acid, sulfuric acid, nitric acid, hydrofluoric acid and so on.

Alkali corrosion

Mostly in the sodium and ammonia chemical production process dust, such as sodium chloride, ammonia, sodium carbonate and other conditions. For the power plant, cement plants, waste incineration plant, steel and other areas of flue gas dust appear less.

Oxidative corrosion

Oxidation and corrosion refers to the existence of a certain amount of oxidizing substances when the damage caused by the filter, mainly for the PPS class of oxidative oxidation of the filter can cause damage to the PPS filter oxide nitrogen oxides, oxygen, ozone, Sulfuric acid and so on. The performance of the PPS fiber into a dark and brittle, the appearance of intact, but the sharp decline in strength, only about 200N, close to the end of the life of the filter, loss of filtering effect.

hydrolysis

Hydrolysis is defined as a chemical reaction in which water molecules intervene in the fibers and cause decomposition. Synthetic fibers produced by polycondensation polymers are not resistant to hydrolysis. Including: polyester, polyimide (P84), NOMEX, COMEX.

High temperature, humidity and chemicals, these three factors must exist to activate the hydrolysis. Polyacrylonitrile homopolymer, PPS fiber, PTFE fiber is not produced from polycondensation polymer, often used to replace the hydrolysis of the fiber. Hydrolysis traces are mostly fiber color turbidity, filter bag strong drop, hand can easily tear, sewing thread after hydrolysis, no strength.

high temperature burning

The performance of the high temperature cauterization is mainly due to the high temperature caused by shrinkage severe, severe hardening, and even filter bag surface hole, the main reason for the use of the filter bag conditions in the temperature beyond the bag to withstand the range, resulting in this phenomenon. Specifically for high temperature particles, high temperature flue gas, high temperature heat shrinkage bag caused by excessive damage to the filter.

condensation obstruction

The so-called condensation, in layman's terms, refers to the wet air in a certain pressure and temperature, precipitation of saturated water phenomenon. The temperature of the precipitation of water is called dew point.

The higher the gas pressure in the saturated state, the lower the dew point. The higher the moisture content in the air, the higher the dew point temperature. When the moisture content in the air is constant, when the temperature of the humidified air is lower than the dew point temperature, the moisture will precipitate in the supersaturated air, that is, the condensation will occur. When the air temperature is higher than the dew point, the moisture will not precipitate Does not produce condensation phenomenon. In addition, if the SO2 content is contained in the flue gas, the SO2 content is higher and the dew point of the flue gas is higher.

As the filter bag used in the environment of large moisture, and dust bonded to the surface of the filter bag, filter bag surface of the microporous plug, resulting in high equipment running resistance, filter bag loss of filtration performance. The specific reasons are as follows:

dust leakage phenomenon existsDue to the existence of leakage phenomenon of dust collector, the outside will be a lot of cold air into the dust collector, so that the local temperature of the precipitator drops sharply, the air in the water precipitation, resulting in condensation phenomenon.


Previous: PTFE Filter Bags Reduce Dust Emissions

Next: No Information

Contact Us
Jiangsu Aokai Environmental Technology Co.,Ltd

Address: No.80, Fuqian Road, Chengbei Industrial Park Economic Development Zone, Jingjiang City, Jiangsu Province, China

Tel: +86-523-80235750

Fax: +86-523-80235750

E-mail: mollygu@aokai.net.cn

Copyright © JiangSu AoKai Environmental Technology Co.,Ltd. All Rights Reserved.
foottop